ORAMASK films is a very popular and helpful material for all kinds of painting work. Various types of ORAMASK PVC films are self-adhesive, thanks to which they are easily applied to surface on which we want to carry out painting or sandblasting works. Depending on the type of planned work, we can choose template foils or sandblasting foils.
Note
The working surface on which you want to glue the film must be cleaned of all kinds of dust, grease or other impurities that could cause this product can stick inadequately. Freshly painted or varnished surfaces should be allowed to dry for min. 3 weeks. The possibilities of using selected varnishes or paints with ORAMASK self-adhesive foil should be checked before applying the foil. You should check the chemical reactions between the film and the substrate. Moreover, all information on the application of the foil should be taken into account.
- ORAMASK 810 template film is a transparent gray PVC film
- Film thickness without protective paper and adhesive layer - 80 microns
- The template foil is intended for painting works carried out by brush or spraying on vehicles, painting templates, advertising, market stands
- The film has great flexibility, which makes it perfect for painting not only on even but also on uneven surfaces
- The film uses high-quality polyacrylic adhesive based on solvents, with low final adhesion, which ensures easy and residual removal of the film from the painted surface, e.g. from trailers, even when it is applied wet or when applying several colors paint li>
- The transparency of the gray foil ensures visibility of the veneered surface (elements protected by foil)
- Cover material: One side silicon coated paper, 137 g / m2, ensures easy transfer of film from backing paper to target surface
- Adhesive strength (FINAT test method I, after 24 hours, stainless steel): at least 1 N / 25 mm
- Tear resistance (DIN EN ISO 527):
- longitudinal: min. 19MPa
- transverse: min. 19MPa
- Tensile strength (DIN EN ISO 527)
- longitudinal: min. 130%
- transverse: min. 150%
- Recommended sticking temperature: above +10 o C
- Averaged storage period - approx. 2 years